BIBO Crystal

Crystal Structure

Monoclinic,  Point group C2-2

Lattice Parameter

a = 7.116 Å, b = 4.993 Å, c = 6.508 Å, β = 105.62°, Z = 2

Melting Point

726 ℃

Mohs Hardness

5-5.5 Mohs

Density

5.033 g/cm3

Thermal Expansion Coefficients

αa = 4.8 × 10-5 /K, αb = 4.4 × 10-6 /K, αc = - 2.69 × 10-5 /K

Transparency Range

286 - 2500 nm

Absorption Coefficients

< 0.1%/cm at 1064 nm

Physical Axis

X∥b, (Z, a) = 31.6°, (Y, c) = 47.2°

SHG of 1064/532 nm

Phase matching angle

168.9 ° from Z axis in YZ plane

Deff

3.0 ± 0.1 pm/V

Angular acceptance

2.32 mrad·cm

Walk-off angle

25.6 mrad

Temperature acceptance

2.17 ℃·cm

A

B

C

D

n1

3.6545 (4)

0.0511 (2)

0.0371 (3)

0.0226 (1)

n2

3.0740 (3)

0.0323 (1)

0.0316 (3)

0.01337 (6)

n3

3.1685 (3)

0.0373 (1)

0.0346 (3)

0.01750 (8)

Dimension Tolerance

(W ± 0.1 mm) × (H ± 0.1 mm) × (L + 0.5/-0.1 mm) (L≧2.5 mm)

(W ± 0.1 mm) × (H ± 0. 1 mm ) ×  (L + 0.1/-0.1 mm)  (L＜2.5 mm)

Clear Aperture 

Central 90% of the diameter

Surface Quality (Scratch/Dig)

10/5 to MIL-PRF-13830B

Flatness

≦λ/8 @633 nm

Transmitted Wavefront Distortion

≦λ/8 @633 nm

Parallelism

20 arc sec

Perpendicularity

≦15 arc min

Angle Tolerance

Δθ≦0.25 °, ΔФ≦0.25 °

Chamfer

≦0.2 mm × 45°

Chip

≦0.1 mm

Damage Threshold

＞0.3 GW/cm2 @1064 nm, 10 ns, 10 Hz (AR-Coated)

Quality Warranty Period

One year under proper use.